Klassifikaasje per produksjemetoade
● Naadloos
● Lassen
Klassifikaasje per lasmetoade
● ERW
● SAWL
● SSAW
Grutte berik
Type | OD | Dikte |
NAADLOOS | Ø33,4-323,9 mm (1-12 inch) | 4,5-55 mm |
ERW | Ø21.3-609.6mm (1/2-24 inch) | 8-50mm |
SAWL | Ø457.2-1422.4mm (16-56 inch) | 8-50mm |
SSAW | Ø219.1-3500mm (8-137.8 inch) | 6-25.4mm |
Lykweardige graden
Standert | Klasse | |||||||||
API 5L | A25 | Gr A | GrB | X42 | X46 | X52 | X56 | 60 | 65 | 70 |
GB/T 9711 ISO 3183 | L175 | L210 | L245 | L290 | L320 | L360 | L390 | L415 | L450 | L485 |
Gemyske gearstalling
Gemyske gearstalling foar PSL 1 piip mei t ≤ 0.984"
Stielgraad | Massafraksje, % basearre op waarmte- en produktanalyses a,g | |||||||
C | Mn | P | S | V | Nb | Ti | ||
maks b | maks b | maks | maks | maks | maks | maks | ||
Naadleaze piip | ||||||||
A | 0.22 | 0.9 | 0.3 | 0.3 | – | – | – | |
B | 0.28 | 1.2 | 0.3 | 0.3 | c,d | c,d | d | |
X42 | 0.28 | 1.3 | 0.3 | 0.3 | d | d | d | |
X46 | 0.28 | 1.4 | 0.3 | 0.3 | d | d | d | |
X52 | 0.28 | 1.4 | 0.3 | 0.3 | d | d | d | |
X56 | 0.28 | 1.4 | 0.3 | 0.3 | d | d | d | |
X60 | 0.28 e | 1.40 e | 0.3 | 0.3 | f | f | f | |
X65 | 0.28 e | 1.40 e | 0.3 | 0.3 | f | f | f | |
X70 | 0.28 e | 1.40 e | 0.3 | 0.3 | f | f | f | |
Lassen piip | ||||||||
A | 0.22 | 0.9 | 0.3 | 0.3 | – | – | – | |
B | 0.26 | 1.2 | 0.3 | 0.3 | c,d | c,d | d | |
X42 | 0.26 | 1.3 | 0.3 | 0.3 | d | d | d | |
X46 | 0.26 | 1.4 | 0.3 | 0.3 | d | d | d | |
X52 | 0.26 | 1.4 | 0.3 | 0.3 | d | d | d | |
X56 | 0.26 | 1.4 | 0.3 | 0.3 | d | d | d | |
X60 | 0.26 e | 1.40 e | 0.3 | 0.3 | f | f | f | |
X65 | 0.26 e | 1.45 e | 0.3 | 0.3 | f | f | f | |
X70 | 0.26e | 1,65 e | 0.3 | 0.3 | f | f | f |
in. Cu ≤ = 0,50% Ni; ≤ 0,50%; Cr ≤ 0,50%; en Mo ≤ 0,15%,
b. Foar elke reduksje fan 0,01% ûnder de oantsjutte maksimale konsintraasje foar koalstof, is in ferheging fan 0,05% boppe de oantsjutte maksimale konsintraasje foar Mn tastien, oant in maksimum fan 1,65% foar kwaliteiten ≥ L245 of B, mar ≤ L360 of X52; oant in maksimum fan 1,75% foar kwaliteiten > L360 of X52, mar < L485 of X70; en oant in maksimum fan 2,00% foar kwaliteit L485 of X70.
c. Behalven as oars ôfpraat NB + V ≤ 0,06%,
d. Nb + V + TI ≤ 0,15%,
e. Behalven as oars ôfpraat.,
f. Behalven as oars ôfpraat, NB + V = Ti ≤ 0,15%,
g. Gjin opsetlike tafoeging fan B is tastien en de oerbleaune B ≤ 0,001%
Gemyske gearstalling foar PSL 2-piip mei t ≤ 0,984
Stielgraad | Massafraksje, % basearre op waarmte- en produktanalyses | Koalstofekwivalent | |||||||||
C | Si | Mn | P | S | V | Nb | Ti | Oar | CE IIW | CE Pcm | |
maks b | maks | maks b | maks | maks | maks | maks | maks | maks | maks | ||
Naadleaze piip | |||||||||||
BR | 0.24 | 0.4 | 1.2 | 0.025 | 0.015 | c | c | 0.04 | e,l | 0.43 | 0.25 |
X42R | 0.24 | 0.4 | 1.2 | 0.025 | 0.015 | 0.06 | 0.05 | 0.04 | e,l | 0.43 | 0.25 |
BN | 0.24 | 0.4 | 1.2 | 0.025 | 0.015 | c | c | 0.04 | e,l | 0.43 | 0.25 |
X42N | 0.24 | 0.4 | 1.2 | 0.025 | 0.015 | 0.06 | 0.05 | 0.04 | e,l | 0.43 | 0.25 |
X46N | 0.24 | 0.4 | 1.4 | 0.025 | 0.015 | 0.07 | 0.05 | 0.04 | d, e, l | 0.43 | 0.25 |
X52N | 0.24 | 0.45 | 1.4 | 0.025 | 0.015 | 0.1 | 0.05 | 0.04 | d, e, l | 0.43 | 0.25 |
X56N | 0.24 | 0.45 | 1.4 | 0.025 | 0.015 | 0.10f | 0.05 | 0.04 | d, e, l | 0.43 | 0.25 |
X60N | 0.24f | 0.45f | 1.40f | 0.025 | 0.015 | 0.10f | 0.05f | 0.04f | g, h, l | Lykas ôfpraat | |
BQ | 0.18 | 0.45 | 1.4 | 0.025 | 0.015 | 0.05 | 0.05 | 0.04 | e,l | 0.43 | 0.25 |
X42Q | 0.18 | 0.45 | 1.4 | 0.025 | 0.015 | 0.05 | 0.05 | 0.04 | e,l | 0.43 | 0.25 |
X46Q | 0.18 | 0.45 | 1.4 | 0.025 | 0.015 | 0.05 | 0.05 | 0.04 | e,l | 0.43 | 0.25 |
X52Q | 0.18 | 0.45 | 1.5 | 0.025 | 0.015 | 0.05 | 0.05 | 0.04 | e,l | 0.43 | 0.25 |
X56Q | 0.18 | 0.45f | 1.5 | 0.025 | 0.015 | 0.07 | 0.05 | 0.04 | e,l | 0.43 | 0.25 |
X60Q | 0.18f | 0.45f | 1.70f | 0.025 | 0.015 | g | g | g | h,l | 0.43 | 0.25 |
X65Q | 0.18f | 0.45f | 1.70f | 0.025 | 0.015 | g | g | g | h,l | 0.43 | 0.25 |
X70Q | 0.18f | 0.45f | 1.80f | 0.025 | 0.015 | g | g | g | h,l | 0.43 | 0.25 |
X80Q | 0.18f | 0.45f | 1.90f | 0.025 | 0.015 | g | g | g | i,j | Lykas ôfpraat | |
X90Q | 0.16f | 0.45f | 1.9 | 0.02 | 0.01 | g | g | g | j,k | Lykas ôfpraat | |
X100Q | 0.16f | 0.45f | 1.9 | 0.02 | 0.01 | g | g | g | j,k | Lykas ôfpraat | |
Lassen piip | |||||||||||
BM | 0.22 | 0.45 | 1.2 | 0.025 | 0.015 | 0.05 | 0.05 | 0.04 | e,l | 0.43 | 0.25 |
X42M | 0.22 | 0.45 | 1.3 | 0.025 | 0.015 | 0.05 | 0.05 | 0.04 | e,l | 0.43 | 0.25 |
X46M | 0.22 | 0.45 | 1.3 | 0.025 | 0.015 | 0.05 | 0.05 | 0.04 | e,l | 0.43 | 0.25 |
X52M | 0.22 | 0.45 | 1.4 | 0.025 | 0.015 | d | d | d | e,l | 0.43 | 0.25 |
X56M | 0.22 | 0.45f | 1.4 | 0.025 | 0.015 | d | d | d | e,l | 0.43 | 0.25 |
X60M | 0.12f | 0.45f | 1.60f | 0.025 | 0.015 | g | g | g | h,l | 0.43 | 0.25 |
X65M | 0.12f | 0.45f | 1.60f | 0.025 | 0.015 | g | g | g | h,l | 0.43 | 0.25 |
X70M | 0.12f | 0.45f | 1.70f | 0.025 | 0.015 | g | g | g | h,l | 0.43 | 0.25 |
X80M | 0.12f | 0.45f | 1.85f | 0.025 | 0.015 | g | g | g | i,j | .043f | 0.25 |
X90M | 0.1 | 0.55f | 2.10f | 0.02 | 0.01 | g | g | g | i,j | – | 0.25 |
X100M | 0.1 | 0.55f | 2.10f | 0.02 | 0.01 | g | g | g | i,j | – | 0.25 |
a. SMLS t>0.787", CE-limiten sille wêze lykas ôfpraat. De CEIIW-limiten dy't tapast wurde as C > 0.12% en de CEPcm-limiten binne fan tapassing as C ≤ 0.12%,
b. Foar elke fermindering fan 0,01% ûnder it oantsjutte maksimum foar C, is in ferheging fan 0,05% boppe it oantsjutte maksimum foar Mn tastien, oant in maksimum fan 1,65% foar graden ≥ L245 of B, mar ≤ L360 of X52; oant in maksimum fan 1,75% foar graden > L360 of X52, mar < L485 of X70; oant in maksimum fan 2,00% foar graden ≥ L485 of X70, mar ≤ L555 of X80; en oant in maksimum fan 2,20% foar graden > L555 of X80.
c. Behalven as oars ôfpraat Nb = V ≤ 0,06%,
d. Nb = V = Ti ≤ 0,15%,
e. Behalven as oars ôfpraat, Cu ≤ 0,50%; Ni ≤ 0,30% Cr ≤ 0,30% en Mo ≤ 0,15%,
f. Behalven as oars ôfpraat,
g. Behalven as oars ôfpraat, Nb + V + Ti ≤ 0,15%,
h. Behalve as oars ôfpraat, Cu ≤ 0,50% Ni ≤ 0,50% Cr ≤ 0,50% en MO ≤ 0,50%,
ik. Behalve as oars ôfpraat, Cu ≤ 0,50% Ni ≤ 1,00% Cr ≤ 0,50% en MO ≤ 0,50%,
j. B ≤ 0,004%,
k. Behalve as oars ôfpraat, Cu ≤ 0,50% Ni ≤ 1,00% Cr ≤ 0,55% en MO ≤ 0,80%,
l. Foar alle PSL 2-piipkwaliteiten, útsein dy kwaliteiten mei fuotnoten j neamd, jildt it folgjende. Behalven as oars ôfpraat, is gjin opsetlike tafoeging fan B tastien en is oerbleaune B ≤ 0,001%.
Mechanyske eigendom fan API 5l
Easken foar de resultaten fan trektests foar PSL 1-pipen
Piipklasse | Opbringststerkte a | Treksterkte a | Ferlinging | Treksterkte b |
Rt0,5 PSI Min. | Rm PSI Min | (yn 2in Af % min) | Rm PSI Min | |
A | 30.500 | 48.600 | c | 48.600 |
B | 35.500 | 60.200 | c | 60.200 |
X42 | 42.100 | 60.200 | c | 60.200 |
X46 | 46.400 | 63.100 | c | 63.100 |
X52 | 52.200 | 66.700 | c | 66.700 |
X56 | 56.600 | 71.100 | c | 71.100 |
X60 | 60.200 | 75.400 | c | 75.400 |
X65 | 65.300 | 77.500 | c | 77.500 |
X70 | 70.300 | 82.700 | c | 82.700 |
a. Foar tuskenlizzende klasse moat it ferskil tusken de oantsjutte minimale treksterkte en de oantsjutte minimale opbringst foar it piiplichem wêze lykas jûn foar de folgjende hegere klasse. | ||||
b. Foar de tuskenlizzende kwaliteiten moat de oantsjutte minimale treksterkte foar de lasnaad itselde wêze as bepaald foar it lichem mei help fan fuotnoat a. | ||||
c. De oantsjutte minimale ferlinging, Af, útdrukt yn persintaazje en ôfrûne nei it tichtste persintaazje, moat bepaald wurde mei de folgjende fergeliking: | ||||
Wêrby't C 1940 is foar berekkening mei Si-ienheden en 625.000 foar berekkening mei USC-ienheden | ||||
Axc is de tapaslike dwersdoorsnede fan it treksterkte-teststik, útdrukt yn fjouwerkante millimeters (fjouwerkante inch), as folget | ||||
– Foar teststikken mei in sirkelfoarmige dwerstrochsneed, 130 mm2 (0,20 in2) foar teststikken mei in diameter fan 12,7 mm (0,500 in) en 8,9 mm (0,350 in); en 65 mm2 (0,10 in2) foar teststikken mei in diameter fan 6,4 mm (0,250 in). | ||||
– Foar teststikken mei folsleine seksje, de lytste fan a) 485 mm2 (0,75 in2) en b) it dwerstrochsneedoppervlak fan it teststik, ôflaat mei de oantsjutte bûtenste diameter en de oantsjutte wanddikte fan 'e piip, ôfrûne nei de tichtste 10 mm2 (0,10 in2) | ||||
– Foar stripteststikken, de lytste fan a) 485 mm2 (0.75 in2) en b) de dwersdoorsnede fan it teststik, ôflaat mei de oantsjutte breedte fan it teststik en de oantsjutte wanddikte fan 'e piip, ôfrûne nei de tichtste 10 mm2 (0.10 in2) | ||||
U is de oantsjutte minimale treksterkte, útdrukt yn megapascals (pûn per fjouwerkante inch) |
Easken foar de resultaten fan trektests foar PSL 2-pipen
Piipklasse | Opbringststerkte a | Treksterkte a | Ferhâlding a,c | Ferlinging | Treksterkte d | ||
Rt0,5 PSI Min. | Rm PSI Min | R10,5IRm | (yn 2 inch) | Rm (psi) | |||
Minimum | Maksimum | Minimum | Maksimum | Maksimum | Minimum | Minimum | |
BR, BN, BQ, BM | 35.500 | 65.300 | 60.200 | 95.000 | 0.93 | f | 60.200 |
X42, X42R, X2Q, X42M | 42.100 | 71.800 | 60.200 | 95.000 | 0.93 | f | 60.200 |
X46N, X46Q, X46M | 46.400 | 76.100 | 63.100 | 95.000 | 0.93 | f | 63.100 |
X52N, X52Q, X52M | 52.200 | 76.900 | 66.700 | 110.200 | 0.93 | f | 66.700 |
X56N, X56Q, X56M | 56.600 | 79.000 | 71.100 | 110.200 | 0.93 | f | 71.100 |
X60N, X60Q, S60M | 60.200 | 81.900 | 75.400 | 110.200 | 0.93 | f | 75.400 |
X65Q, X65M | 65.300 | 87.000 | 77.600 | 110.200 | 0.93 | f | 76.600 |
X70Q, X65M | 70.300 | 92.100 | 82.700 | 110.200 | 0.93 | f | 82.700 |
X80Q, X80M | 80.500 | 102.300 | 90.600 | 119.700 | 0.93 | f | 90.600 |
a. Foar tuskenlizzende kwaliteit, sjoch de folsleine API5L-spesifikaasje. | |||||||
b. foar kwaliteiten > X90, ferwize nei de folsleine API5L-spesifikaasje. | |||||||
c. Dizze limyt jildt foar taarten mei D> 12.750 yn | |||||||
d. Foar tuskenlizzende kwaliteiten moat de oantsjutte minimale treksterkte foar de lasnaad deselde wearde wêze as dy't bepaald is foar it piiplichem mei foet a. | |||||||
e. foar piip dy't longitudinale testen fereasket, moat de maksimale reksterkte ≤ 71.800 psi wêze | |||||||
f. De oantsjutte minimale ferlinging, Af, útdrukt yn persintaazje en ôfrûne nei it tichtste persintaazje, moat bepaald wurde mei de folgjende fergeliking: | |||||||
Wêrby't C 1940 is foar berekkening mei Si-ienheden en 625.000 foar berekkening mei USC-ienheden | |||||||
Axc is de tapaslike dwersdoorsnede fan it treksterkte-teststik, útdrukt yn fjouwerkante millimeters (fjouwerkante inch), as folget | |||||||
– Foar teststikken mei in sirkelfoarmige dwerstrochsneed, 130 mm2 (0,20 in2) foar teststikken mei in diameter fan 12,7 mm (0,500 in) en 8,9 mm (0,350 in); en 65 mm2 (0,10 in2) foar teststikken mei in diameter fan 6,4 mm (0,250 in). | |||||||
– Foar teststikken mei folsleine seksje, de lytste fan a) 485 mm2 (0,75 in2) en b) it dwerstrochsneedoppervlak fan it teststik, ôflaat mei de oantsjutte bûtenste diameter en de oantsjutte wanddikte fan 'e piip, ôfrûne nei de tichtste 10 mm2 (0,10 in2) | |||||||
– Foar stripteststikken, de lytste fan a) 485 mm2 (0.75 in2) en b) de dwersdoorsnede fan it teststik, ôflaat mei de oantsjutte breedte fan it teststik en de oantsjutte wanddikte fan 'e piip, ôfrûne nei de tichtste 10 mm2 (0.10 in2) | |||||||
U is de oantsjutte minimale treksterkte, útdrukt yn megapascal (pûn per fjouwerkante inch) | |||||||
g. Legere wearden foar R10,5IRm kinne by oerienkomst oantsjutte wurde | |||||||
h. foar graden > x90, ferwize nei de folsleine API5L-spesifikaasje. |
Oanfraach
De linepipe wurdt brûkt foar it ferfier fan wetter, oalje en gas foar de petroleum- en ierdgasyndustry.
JINDALAI STEEL leveret kwalifisearre naadleaze en laske pipen neffens de noarmen fan API 5L, ISO 3183, en GB/T 9711.
Detailtekening


-
A106 Crosshole Sonic Logging Laske Buis
-
API 5L KLAS B PIIP
-
ASTM A106 klasse B naadleaze piip
-
A106 GrB Naadloze Grouting Stielen Pipen foar Stapel
-
ASTM A53 Crosshole Sonic Logging (CSL) lassen piip
-
SSAW stielen piip / spiraallaspiip
-
4140 Alloy Stielbuis & AISI 4140 Pipe
-
Hege presyzje stielen piip
-
ASME SA192 Boilerpipen/A192 Naadleaze stielen piip
-
SA210 Naadleaze stielen boilerbuis